Quartz Rod hmanga siam a ni

OD range(mm) a ni.

OD tolerance(mm) a ni.

Ovaality a ni

Kun

OD 5.0 ​​aia tlem emaw, a tlukpui emaw

±2.00%OD a ni

2.00%

0.20%

5.0

±1.00%OD a ni

1.00%

0.10%

10.0/OD/20.0 a ni

±1.00%OD a ni

1.00%

0.10%

20.0/OD/30.0 a ni

±1.00%OD a ni

1.00%

0.10%

30.0/OD/50.0 a ni

±1.00%OD a ni

1.00%

0.10%

50.0/OD/100.0 a ni

±1.00%OD a ni

1.00%

0.15%

100.0/OD/160.0 a ni

±1.00%OD a ni

1.00%

0.15%

Code a ni

Khaikhinna

Al

Ca

Cr

Cu

Fe

K

PQ191E a ni

Thuhmun

13.0

0.50

<0.05

<0.05

0.10

0.10

Maximum a ni

19.0

1.00

0.10

0.10

0.50

1.00

PQ191EH a ni

Thuhmun

8.0

0.60

<0.05

<0.01

0.10

0.10

Maximum a ni

10.0

1.00

0.10

<0.01

0.50

0.50

Code a ni

Khaikhinna

Li

Mg

Mn

Na

Ti

Zr

PQ191E a ni

Thuhmun

0.3

0.05

0.05

0.10

1.30

1.00

Maximum a ni

1.00

0.20

0.20

1.00

2.00

2.00

PQ191EH a ni

Thuhmun

0.20

0.05

0.05

0.10

1.30

1.00

Maximum a ni

0.50

0.20

0.20

0.50

2.00

2.00

Taksa lam thil neih (Pysical Properties).

Hlutna (value) te

Thianghlimna

＞99.99%

Sakhal zawng

2.2g/cm a ni³

Transparency a ni

＞90%

Mohs Hardness a ni

5.5--6.5

Deformation Point a ni

1280℃a ni

Softening Point a ni

1750℃a ni

Annealing Point a ni

1250℃a ni

A lumna bik (20 - 350℃) .

670J/kg a ni. degree

A rilru a buai em em a, a rilru a hah em em bawk a. 20℃) .

1.4W/m a ni. degree

A chhuahna tur hmun (w/mk,1000℃) .

1.0-1.2

Refractive Index a ni

1.4585

A rilru a buai em em a, a rilru a hah em em bawk a. Coefficient of Thermal Expansion

5.510 ^-7cm/cm a ni. degree

Hot - hnathawhna Temperature

1750--2050℃thleng a ni

Hun rei lote - chhunga Service Temperature

1450℃a ni

Hun rei tak - chhung Service Temperature

1100℃a ni

Chemical lama thil awm dan

Hlutna (value) te

Acid laka a him lo

Acid chak tak(HF tih loh chu),Alkali chak tak, organic solution

Temperature sang takah Corrosion resistant a awm thei

A tha lutuk

Metal bawlhhlawh awm zat

<5 ppm a ni

Electric lama thil awm dan

Hlutna (value) te

Resistivity (resistivity) a ni

710⁷Ω.cm a ni

Insulation chakna

250~400Kv/cm a ni

Dielectric Constant hmanga siam a ni

3.7~3.9

Dielectric Absorption Coefficient a ni a, a chhuahna tur hmun leh a hmanna tur a ni

＜410^-4

Dielectric hloh zat (Dielectric loss Coefficient) a ni

＜110^-4

Mechanical lama thil awm dan

Hlutna (value) te

Compressive chakna a nei

1100MPa a ni

Bending chakna

67MPa a ni

Tensile chakna a nei

48MPa a ni

Poisson-a Ratio a ni

0.14~0.17

Young-a Modulus a ni

72000MPa a ni

Shear Modulus a ni

31000MPa a ni